Hostaphan® RHS Polyester Film
|
|
A coextruded
polyester film with one surface modified to be heat sealable against itself and
other PET film surfaces. The reverse surface exhibits the same properties of
standard polyester film.
|
|
|
|
|
|
Hostaphan® RHS Polyester Film
|
|
A coextruded
polyester film with one surface modified to be heat sealable against itself and
other PET film surfaces. The reverse surface exhibits the same properties of
standard polyester film.
|
|
PROPERTY
|
UNIT OF MEASURE
|
TYPICAL VALUE
|
TEST METHOD
|
||
|
Thickness
|
Gauge
|
48
|
|
|
|
|
Transparency
|
|
%
|
>90
|
ASTM – D 1003-61
|
|
|
Haze
|
|
%
|
1.5 (12 um)
|
Method A
|
|
|
Brightness 20°
|
|
|
rd. 200
|
DIN 76530
|
|
|
Tensile Strength
|
MD
|
N/mm2
|
280
|
DIN 53455
|
|
|
|
TD
|
|
280
|
Test speed, 100%/min,23°C, 50%RH
|
|
|
Tensile stress required to
|
MD
|
N/mm2
|
110
|
DIN 53455
|
|
|
Cause 5% elongation
|
TD
|
|
110
|
Test speed, 100%/min,23°C, 50%RH
|
|
|
Ultimate Elongation
|
MD
|
%
|
110
|
DIN 53455
|
|
|
|
TD
|
|
90
|
Test speed, 100%/min,23°C, 50%RH
|
|
|
Youngs Modules
|
MD
|
N/mm2
|
4700
|
DIN 53457
|
|
|
|
TD
|
|
5600
|
Test speed, 100%/min,23°C, 50%RH
|
|
|
Roughness Ra
|
Side A nm
|
60
|
DIN 4762
|
|
|
|
|
Side C nm
|
20
|
Cut off 0.25 mm
|
||
|
Coefficient of Friction
|
Side A/A
|
0.6 – 0.7
|
DIN 53375
|
|
|
|
|
Side A/C
|
0.3 – 0.4
|
|
|
|
|
|
Side C/C
|
0.3 – 0.4
|
|
|
|
|
Shrinkage
|
MD
|
%
|
1.3
|
DIN 40634
|
|
|
|
TD
|
|
0.1
|
150°C, 15min
|
|
|
Sealing Temperature
|
|
°C
|
>120
|
|
|
|
Sealing Strength
|
|
N/15mm
|
Ca. K172 - 3
|
|
|
|
CONDITIONS: Values are for reference only.
Determination of the suitability of the material to the use contemplated is the
user’s responsibility. Users assume all risks resulting from the use of
our products and must confirm adaptability through their own tests. Liability
will in no event exceed value of the material sold.
Hostaphan® is the registered trademark of the
Mitsubishi Polyester Film, LLC.
|
|
|