Hostaphan® 2CSR Polyester Film
|
|
A film with
moderate haze, that is chemically primed on one side for enhanced adhesion. It
combines high strength and flexibility, good dimensional stability and excellent
chemical resistance.
|
|
|
|
|
|
Hostaphan® 2CSR Polyester Film
|
|
A film with
moderate haze, that is chemically primed on one side for enhanced adhesion. It
combines high strength and flexibility, good dimensional stability and excellent
chemical resistance.
|
|
Property
|
|
Unit of Measure
|
Typical Value
|
Test Method
|
|
Area Yield
|
|
In2•mil/lb
|
19,800
|
ASTM D 4321
|
|
|
|
in2•mm/kg
|
171
|
|
|
Tensile Strength
|
MD
|
psi
|
32,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
2,250
|
|
|
Yield Strength (F5)
|
MD
|
psi
|
15,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
1,050
|
|
|
Ultimate Elongation
|
MD
|
%
|
100
|
ASTM D 882
|
|
Modulus
|
MD
|
psi
|
600,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
42,200
|
|
|
Coefficent of Friction A/B
|
(Static)
|
|
0.40
|
ASTM D 1894
|
|
|
(Kinetic)
|
|
0.37
|
|
|
Shrinkage
|
MD
|
%
|
1.5
|
30 min. at 150°C
|
|
|
TD
|
%
|
0.4
|
|
|
Tear Strength
|
|
g/mil
|
20
|
ASTM D 1992
|
|
|
|
g/cm
|
0.8
|
|
|
Moisture Vapor Transmission Rate
|
|
g/100 in2•24hr
|
2.8
|
ASTM E 96, E
|
|
|
|
g/m2•24hr
|
43
|
|
|
Oxygen Transmission Rate
|
|
g/100 in2•24hr•atm
|
6.1
|
ASTM D 3985
|
|
|
|
cc/m2•24hr•atm
|
94
|
|
|
Density
|
|
g/cm3
|
1.395
|
ASTM D 1505
|
|
Total Haze
|
48 gauge
|
%
|
4.5
|
ASTM D 1003
|
|
*Values are for reference only. Contact your Pilcher
Hamilton Sales Representative for actual gauges available.
|
|||
|
|
|||
|
Performance
|
|
FDA Status
|
|
|
Hostaphan® 2CSR has excellent slip and good dimensional
stability over a wide temperature range. The primed surface provides enhanced
adhesion to solvent based inks, coatings, and adhesives, as well as vacuum
deposited metal, 2CSR can be coated or metallized to enhance barrier properties
and is designed specifically for use in packaging applications.
|
|
The plain side as well as the chemically primed side of Hostaphan®
2CSR can be used for direct food contact applications subject to
limitations found in 21 CFR 177.1630(f) and in accordance with good
manufacturing practices. Contact your Pilcher Hamilton Representative for more
information.
|
|
|
|
|||
|
CONDITIONS: Determination of the suitability of the
material to the use contemplated is the user’s responsibility. Users
assume all risks resulting from the use of our products and must confirm
adaptability through their own tests. Liability will in no event exceed value of
the material sold.