PHanex® CT Polyester Film
|
|
A one-side
corona treated polyester film. It is designed for use in adhesive and extrusion
laminations, metallizing, and various coating and packaging
applications.
|
|
|
|
|
|
PHanex® CT Polyester Film
|
|
A one-side
corona treated polyester film. It is designed for use in adhesive and extrusion
laminations, metallizing, and various coating and packaging
applications.
|
|
PROPERTY
|
UNIT OF MEASURE
|
TYPICAL VALUE
|
TEST METHOD
|
|
|
Yield
|
|
in2 /lb.
|
41,250
|
|
|
Tensile Strength
|
MD
|
psi
|
44,082
|
ASTM D 882
|
|
|
TD
|
psi
|
37,683
|
|
|
Ultimate Elongation
|
MD
|
%
|
115.0
|
ASTM D 882
|
|
|
TD
|
%
|
130.0
|
|
|
F - 5 Value
|
MD
|
psi
|
17,064
|
ASTM D 882
|
|
|
TD
|
psi
|
15,642
|
|
|
Tensile Modulus
|
MD
|
psi
|
455,136
|
ASTM D 882
|
|
|
TD
|
psi
|
455,136
|
|
|
Heat Shrinkage
|
MD
|
%
|
6.0
|
ASTM D 2305
|
|
(10min, 392 °F)
|
TD
|
%
|
1.0
|
|
|
Friction Coefficient
|
US
|
|
0.35
|
ASTM D 1894
|
|
|
UK
|
|
0.45
|
|
|
Moisture Vapor Transmission
|
g/100 in2 •24 hr
|
2.8
|
ASTM E 96 , E
|
|
|
Rate
|
|
g/m2 •24 hr
|
43
|
|
|
Oxygen Transmission Rate
|
|
cc/100 in2 •24 hr•atm
|
6.1
|
ASTM D 3965
|
|
|
|
cc/m2 •24 hr•atm
|
94
|
|
|
Wetting Tension
|
Treated
|
dyne/mc
|
54.0
|
ASTM D 2578
|
|
Haze
|
|
48 Gauge
|
2.0%
|
ASTM D 1003
|
|
* Values are for reference only. Contact your Pilcher
Hamilton Sales Representative for actual gauges available.
|
|
|
|
|
FDA Status |
|
|
PHanex® CT can be used for direct food contact applications
subject to limitations found in 21 FCR 177.1630 and in accordance with good
manufacturing practices. USDA acceptance and drug master file information is
available on request.
|
|
|
|
|
|
CONDITIONS: Determination of the suitability of the
material to the use contemplated is the user’s responsibility. Users
assume all risks resulting from the use of our products and must confirm
adaptability through their own tests. Liability will in no event exceed value of
the material sold.
PHanex® is the registered trademark of The
Pilcher Hamilton Corporation.
|
|
|
pgf_002_phanex_ct-48
|
9/99
|