Hostaphan® 24EB
Polyester Film
|
|
One side chemically primed polyester film for
improved oxygen barrier properties. |
|
PROPERTY |
UNIT OF MEASURE |
TYPICAL VALUE |
TEST METHOD |
|
|
Area
Yield |
48 Gauge |
in2/lb |
41,250 |
ASTM D 4321 |
|
|
|
in2/kg |
717 |
|
|
Tensile
Strength |
MD |
psi |
32,000 |
ASTM D 882 |
|
|
|
kg/cm2 |
2,250 |
|
|
Yield
Strength (F5) |
MD |
psi |
15,500 |
ASTM D 882 |
|
|
|
kg/cm2 |
1,090 |
|
|
Ultimate
Elongation |
MD |
% |
100 |
ASTM D 882 |
|
Modulus |
MD |
psi |
600,000 |
ASTM D 882 |
|
|
|
kg/cm2 |
42,200 |
|
|
Coefficient
of Friction A/B |
(Static) |
- |
0.40 |
ASTM D 1894 |
|
|
(Kinetic) |
|
0.37 |
|
|
Shrinkage |
MD |
% |
1.9 |
30 min. at 150¡C |
|
|
TD |
|
0.4 |
|
|
Oxygen
Transmission Rate |
48 Gauge |
cc/100 in2 24 hráatm |
<0.5 |
ASTM D3985 (see discussion
concerning measurement method) |
|
|
|
cc / m224hráatm |
<7.8 |
|
|
Oxygen
Transmission Rate |
48 Gauge |
cc/100 in224 hráatm |
<0.02 |
ASTM D 3985 |
|
(Metallized Ð 2.4 OD) |
|
cc / in224hráatm |
<0.3 |
|
|
Water
Vapor Transmission Rate |
48 Gauge |
g /100 in224 hr |
3.4 |
ASTM E 96, E |
|
|
|
g / m224hr |
53 |
|
|
Tear
Strength |
MD |
g /mil |
20 |
ASTM D 1922 |
|
|
|
g /um |
0.8 |
|
|
Density |
|
g/cm3 |
1.395 |
ASTM D 1505 |
|
|
|
|
|
|
|
Total
Haze |
48 Gauge |
% |
3.5 |
ASTM D-1003 |
|
FDA status (submitted for approval). The coated side of Hostaphan® 24EB can be used for in-direct food contact applications subject to limitations found in 21 CFR 177.1630 and in accordance with good manufacturing practices. |
CONDITIONS: Determination of the suitability of the material to the use contemplated is the user's responsibility. Users assume all risks resulting from the use of our products and must confirm adaptability through their own tests. Liability will in no event exceed value of the material sold. Hostaphan® is the registered trademark of Mitsubishi Polyester Film Co. | |
|
|