Melinex® 339 Polyester Film
|
|
An opaque white
film with superb handling properties, pretreated on both sides to promote
adhesion to most industrial coatings.
|
|
|
|
|
|
Melinex® 339 Polyester Film
|
|
An opaque white
film with superb handling properties, pretreated on both sides to promote
adhesion to most industrial coatings.
|
|
PROPERTY
|
|
GAUGE
|
VALUES
|
UNITS
|
TEST
|
|
OPTICAL
|
|
|
|
|
|
|
Gloss 45 Degrees
|
|
|
35
|
%
|
ASTM D 1003
|
|
Gloss 60 Degrees
|
|
|
45
|
%
|
ASTM D 1003
|
|
TLT
|
|
500
|
6
|
%
|
ASTM D 1003
|
|
|
|
1000
|
2
|
%
|
ASTM D 1003
|
|
|
|
200
|
12
|
%
|
ASTM D 1003
|
|
|
|
300
|
9
|
%
|
ASTM D 1003
|
|
Whiteness
|
|
200
|
100
|
|
ASTM E 313-79
|
|
|
|
300
|
100
|
|
ASTM E 313-79
|
|
PHYSICAL
|
|
|
|
|
|
|
Density
|
|
< = 140
|
|
g/cm3
|
ASTM D 1505
|
|
|
|
> = 800
|
|
g/cm3
|
ASTM D 1505
|
|
|
|
200 – 300
|
|
g/cm3
|
ASTM D 1505
|
|
|
|
380 – 700
|
|
g/cm3
|
ASTM D 1505
|
|
Slip (static friction)
|
|
|
0.4
|
|
ASTM D 1894-78 (DuPont method)
|
|
Elongation at Break
|
MD
|
|
120
|
%
|
ASTM D 882A
|
|
|
TD
|
|
120
|
%
|
ASTM D 882A
|
|
Tensile Strength
|
MD
|
|
22,000
|
psi
|
ASTM D 882A
|
|
|
TD
|
|
24,200
|
psi
|
ASTM D 882A
|
|
Yield
|
MD
|
|
12,000
|
psi
|
ASTM D 882A
|
|
|
TD
|
|
12,000
|
psi
|
ASTM D 882A
|
|
THERMAL
|
|
|
|
|
|
|
Shrinkage
|
MD
|
|
2.0
|
%
|
Unrestrained @ 190°C/5
min
|
|
|
TD
|
|
1.0
|
%
|
Unrestrained @ 190°C/5
min
|
|
* Values are for reference only. Contact your Pilcher
Hamilton Sales Representative for actual gauges available.
|
|
|
|
|
|
CONDITIONS: Determination of the suitability of the
material to the use contemplated is the user’s responsibility. Users
assume all risks resulting from the use of our products and must confirm
adaptability through their own tests. Liability will in no event exceed value of
the material sold.
Melinex® is the registered trademark of the
DuPont Teijin Films Corporation.
|
|
|
mowpf_012_dupont_melinex_ 339
|
9/00
|