Melinex® 377 Polyester Film
|
|
A translucent
matte film having a medium surface gloss which is suitable for creating wood
grain and muted metallic effects.
|
|
|
|
|
|
Melinex® 377 Polyester Film
|
|
A translucent
matte film having a medium surface gloss which is suitable for creating wood
grain and muted metallic effects.
|
|
PROPERTY
|
|
GAUGE
|
VALUES
|
UNITS
|
TEST
|
|
Gardner Haze
|
|
75
|
66
|
%
|
ASTM D 1003
|
|
|
|
92
|
73
|
%
|
ASTM D 1003
|
|
|
|
142
|
78
|
%
|
ASTM D 1003
|
|
|
|
200
|
95
|
%
|
ASTM D 1003
|
|
|
|
300
|
97
|
%
|
ASTM D 1003
|
|
OPTICAL
|
|
500
|
99
|
%
|
ASTM D 1003
|
|
Gloss 45 Degrees
|
|
92
|
38
|
%
|
ASTM D 523
|
|
Gloss 60 Degrees
|
|
92
|
40
|
%
|
ASTM D 523
|
|
|
|
75
|
79
|
%
|
ASTM D 1003
|
|
|
|
92
|
78
|
%
|
ASTM D 1003
|
|
|
|
142
|
76
|
%
|
ASTM D 1003
|
|
|
|
200
|
70
|
%
|
ASTM D 1003
|
|
|
|
300
|
67
|
%
|
ASTM D 1003
|
|
TLT
|
|
500
|
60
|
%
|
ASTM D 1003
|
|
PHYSICAL
|
|
|
|
|
|
|
C.O.F. (dynamic) A-B
|
|
|
0.3
|
|
ASTM D 1894
|
|
Elongation at Break
|
MD
|
|
140
|
%
|
ASTM D 882-83
(23°c AT 50% RH,
strain rate)
|
|
|
TD
|
|
100
|
%
|
ASTM D 882-83
(23°c AT 50% RH,
strain rate)
|
|
Tensile Strength
|
MD
|
|
24,900
|
psi.
|
ASTM D 882-83
(23°c AT 50% RH,
strain rate)
|
|
|
TD
|
|
30,600
|
psi.
|
ASTM D 882-83
(23°c AT 50% RH,
strain rate)
|
|
Yield Strength
|
MD
|
|
14,500
|
psi.
|
ASTM D 882A
|
|
|
TD
|
|
15,500
|
psi.
|
ASTM D 882A
|
|
THERMAL
|
|
|
|
|
|
|
Coef. Of Thermal Expansion
|
MD
|
|
19X10E-6
|
cm/cm°C
|
Between 20 -
50°C
|
|
|
TD
|
|
19X10E-6
|
cm/cm°C
|
Between 20 -
50°C
|
|
Shrinkage
|
MD
|
>200
|
3.0
|
%
|
Unrestrained @
190°C/5min
|
|
|
|
75-142
|
3.0
|
%
|
Unrestrained @
190°C/5min
|
|
|
TD
|
>200
|
3.0
|
%
|
Unrestrained @
190°C/5min
|
|
|
|
75-142
|
0.0
|
%
|
Unrestrained @
190°C/5min
|
|
Upper Melt Temperature
|
|
|
491-500
|
°F
|
ASTM E794-85
|
|
* Values are for reference only. Contact your Pilcher
Hamilton Sales Representative for actual gauges available.
|
|
|
|
|
|
CONDITIONS: Determination of the suitability of the
material to the use contemplated is the user’s responsibility. Users
assume all risks resulting from the use of our products and must confirm
adaptability through their own tests. Liability will in no event exceed value of
the material sold.