Excell® XZ32
Polyester Film
|
|
A translucent direct matte film, with low surface gloss.
This film is suitable for stamping foil, metallizing and mold
releasing applications. |
|
PROPERTY |
UNIT OF MEASURE |
TYPICAL VALUES |
TEST METHOD |
|||||||
|
Gauge |
|
|
48 |
75 |
92 |
142 |
200 |
300 |
400 |
Micrometer Method |
|
Tensile
Strength |
MD |
psiX103 |
30 |
30 |
30 |
28 |
26 |
26 |
26 |
|
|
|
TD |
psiX103 |
30 |
30 |
30 |
30 |
30 |
30 |
30 |
|
|
Elongation
at Break |
MD |
% |
90 |
90 |
90 |
130 |
130 |
130 |
140 |
ASTM D 882A |
|
|
TD |
% |
90 |
90 |
90 |
110 |
120 |
120 |
120 |
|
|
Young’s
Modulus |
MD |
psiX103 |
570 |
570 |
570 |
570 |
570 |
570 |
570 |
|
|
|
TD |
psiX103 |
640 |
640 |
640 |
640 |
598 |
598 |
598 |
|
|
Heat
Shrinkage |
MD |
% |
1.5 |
1.5 |
1.5 |
1.0 |
1.0 |
1.0 |
1.0 |
TSI Method (302°F /30min) |
|
|
TD |
% |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
|
|
Haze |
|
% |
72 |
75 |
75 |
83 |
85 |
86 |
88 |
|
|
Total
Luminous Transmission |
|
% |
80 |
80 |
80 |
76 |
74 |
70 |
66 |
ASTM D 1003 |
|
Gloss
(60°) |
|
% |
35 |
29 |
29 |
28 |
28 |
28 |
28 |
ASTM D 523 |
|
Density |
|
- |
1.4 |
1.4 |
1.4 |
1.4 |
1.4 |
1.4 |
1.4 |
ASTM D 1505 |
|
*
Values are for reference only.
Contact your Pilcher Hamilton Sales Representative for actual gauges
available. CONDITIONS: Determination of the
suitability of the material to the use contemplated is the user’s
responsibility. Users assume all
risks resulting from the use of our products and must confirm adaptability
through their own tests. Liability
will in no event exceed value of the material sold. Excell®
is the registered trademark of Toray Saehan Inc. |
|
|
|
11/02 |