PHanex® IMC Polyester Film
|
|
A clear
polyester film that is untreated on either side. It combines high strength and
durability, optical clarity and excellent chemical resistance.
|
|
|
|
|
|
PHanex® IMC Polyester Film
|
|
A clear
polyester film that is untreated on either side. It combines high strength and
durability, optical clarity and excellent chemical resistance.
|
|
PROPERTY
|
UNIT OF MEASURE
|
TYPICAL VALUE
|
TEST METHOD
|
|
|
Area Yield
|
|
in2•mil/lb.
|
19,800
|
ASTM D 4321
|
|
|
|
m2•mm/kg
|
717
|
|
|
Tensile Strength
|
MD
|
psi
|
30,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
2,110
|
|
|
Yield Strength (F5)
|
MD
|
psi
|
15,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
1,050
|
|
|
Ultimate Elongation
|
MD
|
%
|
150
|
ASTM D 882
|
|
Modules
|
MD
|
psi
|
500,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
35,200
|
|
|
Coefficient of Friction A/B
|
(Kinetic)
|
-
|
0.40
|
ASTM D 1894
|
|
Shrinkage
|
MD
|
%
|
1.2
|
30 min. at 150°C
|
|
|
TD
|
|
0.0
|
|
|
Dyne Level
|
|
|
40-44
|
|
|
Density
|
|
g/cm3
|
1.395
|
ASTM D 1505
|
|
Total Haze
|
200 Gauge
|
2.5%
|
|
ASTM D 1003
|
|
|
265 Gauge
|
3.0%
|
|
|
|
|
380 Gauge
|
3.5%
|
|
|
|
|
460 Gauge
|
4.0%
|
|
|
|
* Values are for reference only. Contact your Pilcher
Hamilton Sales Representative for actual gauges available.
|
|
|
|
|
|
CONDITIONS: Determination of the suitability of the
material to the use contemplated is the user’s responsibility. Users
assume all risks resulting from the use of our products and must confirm
adaptability through their own tests. Liability will in no event exceed value of
the material sold.
PHanex® is the registered trademark of The
Pilcher Hamilton Corporation.
|
|
|
IEGPF_008_Phanex_IMC
|
1/00
|