Hostaphan® 2SLK Coated Polyester
Film
|
|
A film with
moderate haze; that is silicone coated on one side. Along with high strength,
flexibility, and chemical resistance, this product provides excellent slip and
good dimensional stability over a wide temperature range. Not FDA
approved.
|
|
PROPERTY
|
UNIT OF MEASURE
|
TYPICAL VALUE
|
TEST METHOD
|
|||
|
Area Yield
|
|
in2•mil/lb.
|
19,800
|
ASTM D 4321
|
||
|
|
m2•mm/kg
|
717
|
|
|||
|
Tensile Strength
|
MD
|
psi
|
30,000
|
ASTM D 882
|
||
|
|
kg/cm2
|
2,100
|
|
|||
|
Yield Strength (F5)
|
MD
|
psi
|
15,000
|
ASTM D 882
|
||
|
|
kg/cm2
|
1,050,
|
|
|||
|
Ultimate Elongation
|
MD
|
%
|
115
|
ASTM D 882
|
||
|
Modules
|
MD
|
psi
|
550,000
|
ASTM D 882
|
||
|
|
kg/cm2
|
38,700
|
|
|||
|
Coefficient of Friction A/B
|
(Kinetic)
|
-
|
0.20
|
ASTM D 1894
|
||
|
Shrinkage
|
MD
|
%
|
1.5
|
30 min. at 150°C
|
||
|
TD
|
|
0.4
|
|
|||
|
Density
|
|
g/cm3
|
1.395
|
ASTM D 1505
|
||
|
Total Haze
|
92 gauge
|
7.5%
|
7.5
|
ASTM D 1000
|
||
|
|
142 Gauge
|
10.5%
|
10.5
|
|
||
|
SILICONE FUNCTIONALITY
|
||||||
|
Smear
|
g/in
|
3 to 10
|
T-peel from em 610 and TESA 415 tape @ 12 in./min.
|
|||
|
|
10 to 30
|
T-peel from BOPP/Getva 1753 adhesive @ 12 in./min.
|
||||
|
Smear
|
-
|
None
|
Haze observed when rubbed once with index finger
|
|||
|
Rub-off
|
-
|
None
|
Coating removed when rubbed hard with index finger
|
|||
|
Migration
|
-
|
None
|
Effect on tackiness of 3M 610 tape after contact with silicone
coating
|
|||
|
Re-adhesion
|
%
|
>95
|
Peel force of TESA 4154 tape to stainless steel after contact with
silicone coating
|
|||
|
* Values are for reference only. Contact your Pilcher
Hamilton Sales Representative for actual gauges available.
|
|
|
|
|
|
CONDITIONS: Determination of the suitability of the
material to the use contemplated is the user’s responsibility. Users
assume all risks resulting from the use of our products and must confirm
adaptability through their own tests. Liability will in no event exceed value of
the material sold.