PHanex® EWC Polyester Film
|
|
An electrical
grade polyester that is untreated on either side. It combines high strength and
durability, good dimensional stability and excellent chemical
resistance.
|
|
|
|
|
|
PHanex® EWC Polyester Film
|
|
An electrical
grade polyester that is untreated on either side. It combines high strength and
durability, good dimensional stability and excellent chemical
resistance.
|
|
PROPERTY
|
UNIT OF MEASURE
|
TYPICAL VALUE
|
TEST METHOD
|
|
|
Area Yield
|
|
in2•mil/lb.
|
19,800
|
ASTM D 4321
|
|
|
|
m2•mm/kg
|
717
|
|
|
Tensile Strength
|
MD
|
psi
|
30,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
2,110
|
|
|
Yield Strength (F5)
|
MD
|
psi
|
15,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
1,050
|
|
|
Ultimate Elongation
|
MD
|
%
|
150
|
ASTM D 882
|
|
Modules
|
MD
|
psi
|
500,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
35,200
|
|
|
Coefficient of Friction A/B
|
(Kinetic)
|
-
|
0.40
|
ASTM D 1894
|
|
Shrinkage
|
MD
|
%
|
1.2
|
30 min. at 150°C
|
|
|
TD
|
|
0.0
|
|
|
Density
|
|
g/cm3
|
1.395
|
ASTM D 1505
|
|
Dielectric Breakdown
|
Kilovolts
|
48 gauge
|
3.0 min.
|
ASTM D149
|
|
|
|
75 gauge
|
4.8 min.
|
|
|
|
|
92 gauge
|
6.0 min.
|
|
|
|
|
142 gauge
|
8.5 min.
|
|
|
|
|
200 gauge
|
7.7 min.
|
|
|
|
|
400 gauge
|
10.0 min.
|
|
|
|
|
500 gauge
|
12.0 min.
|
|
|
|
|
650 gauge
|
13.5 min.
|
|
|
|
|
750 gauge
|
15.5 min.
|
|
|
|
|
1000 gauge
|
36.0 min.
|
|
|
|
|
1400 gauge
|
32.0 min.
|
|
|
* Values are for reference only. Contact your Pilcher
Hamilton Sales Representative for actual gauges available.
|
|
|
|
|
|
|
|
|
CONDITIONS: Determination of the suitability of the
material to the use contemplated is the user’s responsibility. Users
assume all risks resulting from the use of our products and must confirm
adaptability through their own tests. Liability will in no event exceed value of
the material sold.