Hostaphan® 22PK Coated Polyester Film
|
|
One side silicone coated polyester film reverse
surface is treated to provide slip control. |
|
PROPERTY |
UNIT OF MEASURE |
TYPICAL VALUE |
TEST METHOD |
|
|
Area
Yield |
|
in2- mil/lb |
19,800 |
ASTM D 4321 |
|
|
|
m2- mm/kg |
717 |
|
|
Tensile
Strength |
MD |
psi |
30,000 |
ASTM D 882 |
|
|
|
kg/cm2 |
2,100 |
|
|
Yield
Strength (F5) |
MD |
psi |
15,000 |
ASTM D 882 |
|
|
|
kg/cm2 |
1,050 |
|
|
Ultimate
Elongation |
MD |
% |
115 |
ASTM D 882 |
|
Modulus |
MD |
psi |
550,000 |
ASTM D 882 |
|
|
|
kg/cm2 |
38,700 |
|
|
Coefficient
of Friction A/B |
(Kinetic) |
- |
0.40 |
ASTM D 1894 |
|
Shrinkage |
MD |
% |
1.5 |
30 min. at 150ÁC |
|
|
TD |
|
0.4 |
|
|
Density |
|
g/cm3 |
1.395 |
ASTM D 1505 |
|
Total
Haze* |
92 Gauge |
% |
6.2 |
ASTM D-1003 |
|
|
142 Gauge |
|
8.6 |
|
|
|
||||
|
SILICONE
FUNCTIONALITY |
||||
|
Release
From Silicone Side |
g/in |
|
3 to 10 |
T-peel from 3M 610 and TESA 4154 tape @ 12 in./min. |
|
|
|
|
10 to 30 |
T-peel from BOPP/Gelva 1753 adhesive @ 12 in./min. |
|
Smear |
-- |
|
None |
Haze observed when rubbed once with index finger. |
|
Rub-off |
-- |
|
None |
Coating removed when rubbed hard with index finger. |
|
Migration |
-- |
|
None |
Effect on tackiness of 3M 610 tape after contact with silicone coating. |
|
Re-adhesion |
% |
|
>95 |
Peel force of 3M 610 tape to stainless steel after contact with silicone coating. |
|
* Values are for reference only.Contact your Pilcher Hamilton Sales Representative for actual gauges available. CONDITIONS: Determination of the suitability of the material to the use contemplated is the user's responsibility. Users assume all risks resulting from the use of our products and must confirm adaptability through their own tests. Liability will in no event exceed value of the material sold. Hostaphan® is the registered trademark of Mitsubishi Polyester Film Co. |
|
|
|