PHanex® GZZ Polyester Film
|
|
An ultra clear
polyester film that is chemically treated on both sides to reduce static
propensity and improve handleability. It combines high durability, optical
clarity and balanced shrinkage for improved flatness after thermal
processing.
|
|
PROPERTY
|
UNIT OF MEASURE
|
TYPICAL VALUE
|
TEST METHOD
|
|||||
|
Area Yield
|
|
in2•mil/lb.
|
19,800
|
ASTM D 4321
|
||||
|
|
|
m2•mm/kg
|
717
|
|
||||
|
Tensile Strength
|
MD
|
psi
|
30,000
|
ASTM D 882
|
||||
|
|
|
kg/cm2
|
2,110
|
|
||||
|
Yield Strength (F5)
|
MD
|
psi
|
15,000
|
ASTM D 882
|
||||
|
|
|
kg/cm2
|
1,050
|
|
||||
|
Ultimate Elongation
|
MD
|
%
|
150
|
ASTM D 882
|
||||
|
Modules
|
MD
|
psi
|
500,000
|
ASTM D 882
|
||||
|
|
|
kg/cm2
|
35,200
|
|
||||
|
Coefficient of Friction A/B
|
(Kinetic)
|
-
|
0.40
|
ASTM D 1894
|
||||
|
Shrinkage
|
MD
|
%
|
1.2
|
39 min. at 150°C
|
||||
|
|
TD
|
|
0.0
|
|
||||
|
Density
|
|
g/cm3
|
1.395
|
ASTM D 1505
|
||||
|
Total Haze
|
400 Gauge
|
0.8%
|
|
ASTM D 1000
|
||||
|
|
500 Gauge
|
0.9%
|
|
|
||||
|
|
700 Gauge
|
1.1%
|
|
|
||||
|
ANTI-STAT FUNCTIONALITY
|
||||||||
|
PROPERTY
|
UNIT OF MEASURE
|
TYPICAL VALUE
|
TEST STANDARD SPECIFICATION
|
TEST CONDITIONS
|
||||
|
Surface Resistivity
|
ohms
|
5.0 X 1010
|
ASTM D 257
|
23°C
@ 50% R.H.
|
||||
|
Static Change Decay
|
seconds
|
0.05
|
Federal Test Method Standard
|
23°C
@ 50% R.H.
|
||||
|
|
|
|
No. 101B; Method 4046
|
|||||
|
|
|
|
Equipment; Elector-Tech System;; Model 406C
|
|||||
|
* Values are for reference only. Contact your Pilcher
Hamilton Sales Representative for actual gauges available
|
|
|
|
|
|
CONDITIONS: Determination of the suitability of the
material to the use contemplated is the user’s responsibility. Users
assume all risks resulting from the use of our products and must confirm
adaptability through their own tests. Liability will in no event exceed value of
the material sold.