A very clear
polyester film that is chemically primed on one side to promote adhesion to
solvent based inks and coatings. It combines high strength and durability,
Optical clarity, Good handling characteristics and excellent chemical
resistance.
|
|
|
|
|
|
A very clear
polyester film that is chemically primed on one side to promote adhesion to
solvent based inks and coatings. It combines high strength and durability,
Optical clarity, Good handling characteristics and excellent chemical
resistance.
|
|
PROPERTY
|
UNIT OF MEASURE
|
TYPICAL VALUE
|
TEST METHOD
|
|
|
Area Yield
|
|
In2•mil/lb.
|
19,800
|
ASTM D 4321
|
|
|
|
m2•mm/kg
|
717
|
|
|
Tensile Strength
|
MD
|
psi
|
31,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
2,180
|
|
|
Yield Strength (F5)
|
MD
|
psi
|
15,500
|
ASTM D 882
|
|
|
|
kg/cm2
|
1,090
|
|
|
Ultimate Elongation
|
MD
|
%
|
115
|
ASTM D 882
|
|
Modules
|
MD
|
psi
|
550,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
38,700
|
|
|
Coefficient of Friction A/B
|
(Static)
|
-
|
0.36
|
ASTM D 1894
|
|
|
(Kinetic)
|
-
|
0.34
|
|
|
Shrinkage
|
MD
|
%
|
1.6
|
30 min. at 150°C
|
|
|
TD
|
|
0.7
|
|
|
Density
|
|
g/cm3
|
1.395
|
ASTM D 1505
|
|
Total Haze
|
92 Gauge
|
1.2%
|
|
ASTM D 1000
|
|
|
142 Gauge
|
1.3%
|
|
|
|
|
200 Gauge
|
1.4%
|
|
|
|
* Values are for reference only. Contact your Pilcher
Hamilton Sales Representative for actual gauges available.
|
|
|
|
|
|
CONDITIONS: Determination of the suitability of the
material to the use contemplated is the user’s responsibility. Users
assume all risks resulting from the use of our products and must confirm
adaptability through their own tests. Liability will in no event exceed value of
the material sold.