An ultra clear
polyester film that is chemically primed on one side to improve adhesion of
solvent based inks and coatings and chemically treated on the other side to
reduce static propensity and improve handleability. It combines high strength,
good dimensional stability and excellent chemical resistance.
|
|
PROPERTY
|
UNIT OF MEASURE
|
TYPICAL VALUE
|
TEST METHOD
|
|
|
Area Yield
|
|
in2•mil/lb.
|
19,800
|
ASTM D 4321
|
|
|
|
m2•mm/kg
|
717
|
|
|
Tensile Strength
|
MD
|
psi
|
31,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
2,180
|
|
|
Yield Strength (F5)
|
MD
|
psi
|
15,500
|
ASTM D 882
|
|
|
|
kg/cm2
|
1,050,
|
|
|
Ultimate Elongation
|
MD
|
%
|
115
|
ASTM D 882
|
|
Modules
|
MD
|
psi
|
550,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
38,700
|
|
|
Coefficient of Friction A/B
|
(Static)
|
-
|
0.36
|
|
|
|
(Kinetic)
|
-
|
0.0.43
|
ASTM D 1894
|
|
Shrinkage
|
MD
|
%
|
2.5
|
30 min. at 150°C
|
|
|
TD
|
|
2.5
|
|
|
Density
|
|
g/cm3
|
1.395
|
ASTM D 1505
|
|
Total Haze
|
92 gauge
|
2.0%
|
|
ASTM D 1003
|
|
|
142 gauge
|
2.0%
|
|
|
|
* Values are for reference only. Contact your Pilcher
Hamilton Sales Representative for actual gauges available.
|
|
|
|
|
|
CONDITIONS: Determination of the suitability of the
material to the use contemplated is the user’s responsibility. Users
assume all risks resulting from the use of our products and must confirm
adaptability through their own tests. Liability will in no event exceed value of
the material sold.
PHanex® is the registered trademark of The
Pilcher Hamilton Corporation.
|
|
|
003 Phanex_gaa_92-142
|
6/00
|