PHanex® GCC Polyester Film
|
|
Very clear
polyester film, untreated on either side that provides thin gauge handleability
with excellent clarity and dimensional stability.
|
|
|
|
|
|
PHanex® GCC Polyester Film
|
|
Very clear
polyester film, untreated on either side that provides thin gauge handleability
with excellent clarity and dimensional stability.
|
|
PROPERTY
|
UNIT OF MEASURE
|
TYPICAL VALUE
|
TEST METHOD
|
|
|
Area Yield
|
|
in2•mil/lb.
|
19,800
|
ASTM D 4321
|
|
|
|
m2•mm/kg
|
717
|
|
|
Tensile Strength
|
MD
|
psi
|
33,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
2,320
|
|
|
Yield Strength (F5)
|
MD
|
psi
|
15,500
|
ASTM D 882
|
|
|
|
kg/cm2
|
1,090
|
|
|
Ultimate Elongation
|
MD
|
%
|
105
|
ASTM D 882
|
|
Modules
|
MD
|
psi
|
600,000
|
ASTM D 882
|
|
|
|
kg/cm2
|
42,200
|
|
|
Coefficient of Friction A/B
|
(Kinetic)
|
-
|
0.47
|
ASTM D 1894
|
|
Shrinkage
|
MD
|
%
|
1.3
|
30 min. at 150°C
|
|
|
TD
|
|
0.0
|
|
|
Tear Strength
|
MD
|
g/mil
|
20
|
|
|
|
|
g/mil
|
0.8
|
|
|
Density
|
|
g/cm3
|
1.395
|
ASTM D 1505
|
|
Total Haze
|
48 Gauge
|
1.1%
|
|
ASTM D 1000
|
|
|
92 Gauge
|
1.6%
|
|
|
|
* Values are for reference only. Contact your Pilcher
Hamilton Sales Representative for actual gauges available.
|
|
|
|
|
|
CONDITIONS: Determination of the suitability of the
material to the use contemplated is the user’s responsibility. Users
assume all risks resulting from the use of our products and must confirm
adaptability through their own tests. Liability will in no event exceed value of
the material sold.
PHanex® is the registered trademark of The
Pilcher Hamilton Corporation.
|
|
|
ggpf_001_PHanex_gcc
|
2/99
|